No. Because you will face a whole array of problems, not the least of which is the tearing shown here. This is the first, poor mold release, or more correct, impossible mold release! Plates will be too thin-walled. If you cast them longer wall thickness will be uneven. Edges will crack like this (because of poor plasticity). They will warp during drying. They will lack dry strength for handling. They will warp during firing. You won't be able to get a good rim. You won't be able to cast a foot ring without an indent showing on the inside. Note here that another issue is at play: The clay is either not plastic enough to cut cleanly at the rim, without tearing. Or, it is being cut too late or with a dull knife. These tears provide places for cracks to initiate. Plates are much better made using the jiggering, ram pressing or dust pressing processes. Or by throwing them on plaster batts.