When formulating a white throwing porcelain that employs a white expensive plasticizer (like Bentone or Veegum) the optimal range of percentages can be surprisingly narrow (I am assuming at least 40% kaolin is present). The trimming behavior is one indicator. When there is insufficient plasticizer the tool will chatter (of course in extreme cases edges will tear). Smoothing the corners after trimming (using your finger) will also give you an indication. If there is too much plasticizer, the material will ball up under your finger, if there is insufficient it will not smooth out well. The percentage can be critical: 0.5% too high and the drying shrinkage could sky rocket, 0.5% too low and lips can split at the rim during throwing.