Plaster

Alternate Names: Gypsum, Selenite

Notes

There are many different types of plaster and they vary mainly in setting time, strength, absorbency. Manufacturers provide instruction booklets on how to mix and use their materials. For example, common precautions with reference to pottery plaster are: Don't stack pallets 3 high to avoid hard chunks, use before the shelf life of 120 days expires (if longer then extend mixing time), don't mix at higher than 105 degrees for proper set.

USG Pottery #1 (2000 psi) is an example of an all around material. It is normally mixed at a 70 consistency (70 water to 100 plaster). Jiggering benefits from a plaster with more surface hardening additives (i.e. USG's "Puritan" 66:100 plastic:water). For carving USG "Moulding Plaster" works well. USG Ultracal (5000 psi) and Hyrdostone (10,000 psi) are very hard materials and ideal for case molds where hardness and the expense of absorbency are required (they require much less water).

The optimum hardness and absorbency of the final product are best achieved with the proper water to plaster ratio. Manufacturers recommend that you weigh the water, add the plaster to the water, soak for 2-3 minutes, then mix well using a propeller mixer. It is important not to mix in air bubbles, but to agitate in such a way that the air bubbles break at the surface during mixing.

Gypsum cements are not the same as pottery plasters. They are designed for optimum surface hardening, dimensional stability, and very low expansion.

An continuous plaster mixing machine as available from: Hoge Warren Zimmermann Co., 40 West Crescentville Rd., Cincinnati, OH 45246 FAX 513-671-3514

Plaster dust is not harmful. It is calcium sulphate, or Selenite. Many raw clays contain small chunks of natural Selenite, it just gets ground up with the rest of the clay. If there is significant amounts then you will be able to smell sulphur during firing (but with ventilation in modern kilns this is highly unlikely). If any plaster contamination particles get into your clay the issue you will experience is called "popping". After firing, as a piece absorbs water from the air over time, the particles of gypsum close enough to the surface can expand and pop out a piece of the clay to relieve the pressure.

Related Information

Links

Oxide Analysis Formula
Materials Sodium Selenite
URLs https://en.wikipedia.org/wiki/Plaster
Plaster at Wikipedia
Information on the chemical reactions that occur when gymsum is heated.

By Tony Hansen


Tell Us How to Improve This Page

Or ask a question and we will alter this page to better answer it.

Email Address

Name

Subject

Message


CAPTCHA



https://digitalfire.com, All Rights Reserved
Privacy Policy