We get this clay from St. Rose, Manitoba. Four tandem loads arrived this week. Just seeing the pile inspires me to make more pieces! It is a red fireclay and it is highly unusual. St. Rose Red has issues. They at first seem to be problems, but in combination they give it magic powers! It fires with very heavy iron speckling. The iron pigmentation is so high that it burns almost black at cone 10R. It has low plasticity. It shivers glazes: The vase on this picture lasted an hour after kiln exit, it spontaneously fractured because of the outward pressure from the under-compression glaze on the inside. But, by combining St. Rose Red with our more vitreous clays, which are highly plastic, we can make H440 and H443. But guess what happens when feldspar is added? A mix of 45 St. Rose, 40 Ball clay and 15 feldspar produces a rustic metallic surface (like the cup shown). Such a body cannot be made from a low fire red clay (like RedArt), it would just warp and collapse in the kiln. It is the refractory character, heavy pigmentation, iron speckling and low plasticity of St. Rose that make metallic ware possible.
This is the lump form of Plainsman St. Rose Red clay, as received from the quarry. The bright red color is natural iron oxide. That iron cannot be washed out, it is part of the clay crystal structure. The pigmentation is heavy enough that even when this material is a minor part of a body recipe, that body will still fire to a dark color. The color and high cost of St. Rose Red means that it is always heavily diluted with other clays, many of which are highly plastic. Because St. Rose is non-plastic it is a perfect complement to these. It is also refractory, it melts at a much higher temperature than typical clays. It is mined near St. Rose, Manitoba.
Top to bottom: Cone 10 reduction, cone 10, 9, 8, 7 oxidation. Fire-Red is a mix of St. Rose Red fireclay, M2 Montana medium fire red clay with some dark burning A1 ball clay. This blend is less refractory than pure St. Rose Red and much more plastic, thus more suitable as a body addition. The color shift between cone 9 and 10 oxidation occurs because of the fluxing action of M2.
Both pieces have a transparent glaze, G1947U. The Fire-Red (a blend of Plainsman A1/M2 and St. Rose Red) was mixed as a slurry, dewatered to plastic form and then wedged in to the B-Mix (left piece has 10%, the other 20%, the bar in front shows the pure material). The A1 supplies most of the speckle, the St Rose and M2 impart the color. This addition does not affect the working properties of BMix (it still throws very well). An added benefit is that pieces dry better. Fired strength and maturity are minimally affected (porosity stays around 1%). With a 20% addition the surface of the unglazed clay is almost metallic. Silky matte glazes, like G2571A, are stunning on a body like this.
|Materials||Saint Rose Red|