This body is made from approximately 50:35:15 ball clay:talc:silica:silica sand. These test bars are fired from cone 2 to 9 oxidation (bottom to top) and 10 Reduction and from them the porosity and fired shrinkage can be measured (shown for each bar). Notice that the fired shrinkage is pretty stable from cone 2 to 8, but accelerates at cone 9 oxidation. But in reduction this stage has not been reached yet. The same thing happens with porosity, the cone 9 bar is dramatically more dense than the cone 8 one. But in reduction, it is still porous.
Materials |
Talc
A source of MgO for ceramic glazes, a flux or thermal expansion additive in clay bodies, also used in the manufacture of cordierite. |
Glossary |
Reduction Firing
A method of firing stoneware where the kiln air intakes and burners are set to restrict or eliminate oxygen in the kiln such that metallic oxides convert to their reduced metallic state. |
Glossary |
Vitrification
A process that happens in a kiln, the heat and atmosphere mature and develop the clay body until it reaches a density sufficient to impart the level of strength and durability required for the intended purpose. Most often this state is reached near zero p |
Glossary |
Artware
Potters know artware as pottery firing at low temperatures with brightly coloured glazes and decorated using decals, underglazes, lustres, etc. |