200 mesh | 325 mesh | 3D Design | 3D Printer | 3D Printing Clay | 3D Slicer | 3D-Printing | Abrasion Ceramics | Acidic Oxides | Agglomeration | AI in Ceramics | Alkali | Alkaline Earths | Amorphous | Apparent porosity | Artware | Ball milling | Bamboo Glaze | Base Glaze | Base-Coat Dipping Glaze | Basic Oxides | Batch Recipe | Bisque | Bit Image | Black Core | Bleeding of colors | Blender Mixing | Blunging | Body Bloating | Body glaze Interface | Body Warping | Bone China | Borate | Boron Blue | Boron Frit | Borosilicate | Breaking Glaze | Brick Making | Brushing Glaze | Calcination | Calculated Thermal Expansion | Candling | Carbon Burnout | Carbon trap glazes | CAS Numbers | Casting-Jiggering | Catch Glaze | Celadon Glaze | Ceramic | Ceramic Binder | Ceramic Decals | Ceramic Glaze | Ceramic Glaze Defects | Ceramic Ink | Ceramic Material | Ceramic Oxide | Ceramic Slip | Ceramic Stain | Ceramic Tile | Ceramics | Characterization | Chemical Analysis | Chromaticity | Clay | Clay body | Clay Body Porosity | Clay Stiffness | Clays for Ovens and Heaters | Co-efficient of Thermal Expansion | Code Numbering | Coil pottery | Colloid | Colorant | Commercial hobby brushing glazes | Cone 1 | Cone 5 | Cone 6 | Cone plaque | Copper Red | Cordierite Ceramics | Crackle glaze | Cristobalite | Cristobalite Inversion | Crucible | Crystalline glazes | Crystallization | Cuerda Seca | Cutlery Marking | Decomposition | Deflocculation | Deoxylidration | Differential thermal analysis | Digitalfire API | Digitalfire Foresight | Digitalfire Insight | Digitalfire Reference Library | Digitalfire Taxonomy | Dimpled glaze | Dip Glazing | Dipping Glaze | Dishwasher Safe | Dolomite Matte | Drop-and-Soak Firing | Drying Crack | Drying Performance | Drying Shrinkage | Dunting | Dust Pressing | Earthenware | Efflorescence | Encapsulated Stain | Engobe | Eutectic | Fast Fire Glazes | Fat Glaze | Feldspar Glazes | Fining Agent | Firebrick | Fireclay | Fired Strength | Firing Schedule | Firing Shrinkage | Flameware | Flashing | Flocculation | Fluid Melt Glazes | Flux | Food Safe | Foot Ring | Forming Method | Formula Ratios | Formula Weight | Frit | Fritware | Functional | GHS Safety Data Sheets | Glass vs. Crystalline | Glass-Ceramic Glazes | Glaze Blisters | Glaze Bubbles | Glaze Chemistry | Glaze Compression | Glaze Crawling | Glaze Crazing | Glaze Durability | Glaze fit | Glaze Gelling | Glaze laydown | Glaze Layering | Glaze Mixing | Glaze Recipes | Glaze shivering | Glaze Shrinkage | Glaze thickness | Globally Harmonized Data Sheets | Glossy Glaze | Green Strength | Grog | Gunmetal glaze | High Temperature Glaze | Hot Pressing | Incised decoration | Industrial clay body | Ink Jet Printing | Inside-only Glazing | Insight-Live | Iron Red Glaze | Jasper Ware | Jiggering | Kaki | Kiln Controller | Kiln Firing | Kiln fumes | Kiln venting system | Kiln Wash | Kneading clay | Kovar Metal | Laminations | Leaching | Lead in Ceramic Glazes | Leather hard | Limit Formula | Limit Recipe | Liner Glaze | Liner glazing | Liquid Bright Colors | LOI | Low Temperature Glaze | Majolica | Marbling | Material Substitution | Matte Glaze | Maturity | Maximum Density | MDT | Mechanism | Medium Temperature Glaze | Melt Fluidity | Melting Temperature | Metal Oxides | Metallic Glazes | Micro Organisms | Microwave Safe | Mineral phase | Mineralogy | Mocha glazes | Mohs Hardness | Mole% | Monocottura | Mosaic Tile | Mottled | Mullite Crystals | Native Clay | Non Oxide Ceramics | Oil-spot glaze | Once fire glazing | Opacifier | Opacity | Ovenware | Overglaze | Oxidation Firing | Oxide Formula | Oxide Interaction | Oxide System | Particle orientation | Particle Size Distribution | Particle Sizes | PCE | Permeability | Phase Diagram | Phase Separation | Physical Testing | Pinholing | Plainsman Clays | Plaster Bat | Plaster table | Plasticine | Plasticity | Plucking | Porcelain | Porcelaineous Stoneware | Pour Glazing | Pour Spout | Powder Processing | Precipitation | Primary Clay | Primitive Firing | Propane | Propeller Mixer | Pugmill | Pyroceramics | Pyrometric Cone | Quartz Inversion | Raku | Reactive Glazes | Reduction Firing | Reduction Speckle | Refiring Ceramics | Refractory | Refractory Ceramic Coatings | Representative Sample | Restaurant Ware | Rheology | Rutile Blue Glazes | Salt firing | Sanitary ware | Sculpture | Secondary Clay | Shino Glazes | Side Rails | Sieve | Sieve Shaker | Silica:Alumina Ratio | Silk screen printing | Sintering | Slaking | Slip Casting | Slip Trailing | Slipware | Slurry | Slurry Processing | Slurry Up | Soaking | Soluble colors | Soluble Salts | Specific gravity | Splitting | Spray Glazing | Stain Medium | Stoneware | Stull Chart | Sulfate Scum | Sulfates | Surface Area | Surface Tension | Suspension | Tapper Clay | Tenmoku | Terra Cotta | Terra Sigilatta | Test Kiln | Theoretical Material | Thermal Conductivity | Thermal shock | Thermocouple | Thixotropy | Throwing | Tony Hansen | Toxicity | Trafficking | Translucency | Transparent Glazes | Triaxial Glaze Blending | Ultimate Particles | Underglaze | Unity Formula | Upwork | Variegation | Viscosity | Vitreous | Vitrification | Volatiles | Water Content | Water in Ceramics | Water Smoking | Water Solubility | Wedging | Whiteware | WooCommerce | Wood Ash Glaze | Wood Firing | WordPress | Zero3 | Zero4 | Zeta Potential


Majolica is white opaque glazed red earthenware clay having colored overglaze decoration. But if you know more about what it is technically you will have more control of your product.

Key phrases linking here: majolica - Learn more


Majolica is pottery, almost always decorative and non-functional, fired to a low temperature, employing a red-burning terra cotta clay, covered with a soft opaque white glaze and decorated with colored overglazes. Historically, majolica glazes (or tin glazed earthenware) were opacified using Tin Oxide, but now Zirconium silicate is most often substituted for some or all of the tin. Metallic overglazes are brightest at low temperatures and the zircon/tin white glaze provides an ideal canvas for them. Colorant formulations (mixtures of stain powders, melters, hardeners, fillers) need to be tuned to melt enough so that they become one with the glaze below, but not so much that they bleed excessively at the edge of brush strokes. Different families of stains have different melting behaviors and chemistry requirements for the host glaze and medium (the color development and degree of melting in the final firing product depend on this). You can buy premixed majolica colors and often these work well..

Ware made using the Majolica process is not strong, the clays generally have 10% porosity or more (fired at cone 06-04). This low temperature means that the body-glaze interface is much less developed than for stoneware (so the glaze is not stuck on nearly as well). And, since the glaze is applied so thickly, it has more power to impose its thermal expansion and craze or shiver if it does not fit the body. It is thus important that the thermal expansion of the glaze be matched to the body. Of course ware is not as durable in use so any bare sections will absorb water and tend to water-log the piece over time. It is thus best to make a foot ring so that the entire piece can be glazed, leaving only a narrow channel of exposed body to touch the kiln shelf.

Even application of the base white glaze is critical to the success. This is not possible using paint-on commercial glazes, pieces must be dipped to get, not just even enough coverage, but thick enough. What does "thick enough" mean? It means twice as thick as you thought, far thicker than anything you have ever done. That means it is necessary to mix your own white dipping glaze in quantities sufficient to be able to dip the largest pieces. Dipping can be for 10 or 20 seconds instead of the normal 2-3 seconds! And you need to be able to adjust the rheology of the slurry to get good dipped results. If not, plenty of touch-up time will be required to repair any drips or areas of thicker coverage.

People have different strategies for keeping the glaze in suspension (e.g. the addition of epsom salts to make the slurry thixotropic). Consider this: Since it goes on so thick, if it tries to shrink too much will it have the power to pull itself off and flake? Thus the amount of, and type of, kaolin used is important. Too little kaolin and the glaze will be too powdery, too much and it will shrink excessively. Since fix-up work is commonly needed to remove drips, the glaze must adhere well enough to hang on while you carve away at the surface. If adherence becomes an issue it might be necessary to add some CMC gum, enough to improve adherence and dry hardness but not so much that drying is too slow and a thick enough layer cannot be achieved.

Majolica glaze is remarkably stable as a melt, it stays put, without running. This is why it can be applied so thickly. Yet fires glossy. It is not clear exactly what the mechanism of melt-stiffening is, but it would appear that the high zircon content plays a major role. Ferro Frit 3124 is the one we have most commonly seen in recipes. Ideally it would be good if a fully fritted glaze base could be employed (only frit and kaolin, e.g. G1916Q). However, majolica glazes in common use also have additions of feldspar. This seems like an odd thing to incorporate since the material will not dissolve in the melt at such a low temperature, and it will increase thermal expansion. But the feldspar could be part of the melt-stiffening mechanism and its addition does not impact gloss. That being said, it may also be that 15% zircon in a fully fritted glaze would be enough to stiffen the melt.

Spectrum Glazes makes an excellent line of colored Majolica glazes. These can act both as a stand-alone glaze and as the colors for doing the on-glaze decoration. Typically it is best to use a dipping white that you make yourself and then decorate with these.

Some people add frit to the body, to increase its fired strength. And improve the clay:glaze interface. Such bodies need to be bisque fired much lower (e.g. 200F or more) or they will not be absorbent enough to hold on to the glaze. And it is doubly important that the glaze fits a fritted body, especially that it is not under too much compression. While the thick majolica glaze layer has more power to impose its thermal expansion, the fritted body also has more strength to resist. When the failure finally occurs, it will play out in a fashion more spectacular than simple crazing or shivering: Spontaneous fractures and explosions! With sound effects. Using an expansion-adjustable bases glaze and doing testing is the best way to assure that your clay and glaze are compatible. The EBCT test might work well for this.

Related Information

Test bars of different terra cotta clays fired at different temperatures

Bottom: cone 2, next up: cone 02, next up: cone 04. You can see varying levels of maturity (or vitrification). It is common for terra cotta clays to fire like this, from a light red at cone 06 and then darkening progressively as the temperature rises. Typical materials develop deep red color around cone 02 and then turn brown and begin to expand as the temperature continues to rise past that (the bottom bar appears stable but it has expanded alot, this is a precursor to looming rapid melting). The top disk is a cone 10R clay. It shares an attribute with the cone 02 terra cotta. Its variegated brown and red coloration actually depends on it not being mature, having a 4-5% porosity. If it were fired higher it would turn solid chocolate brown like the over-fired terra cotta at the bottom.

A dried terra cotta mug on the left, bisque fired to cone 06 on the right

These were fired to cone 06, about 1800F. Of course, there is normally some shrinkage so the bisque piece would be a little smaller. Even though the matrix is very porous and is under developed, the iron in the body is already beginning to impose its color.

Bi-Clay strips test compatibility between engobe and body

Slips and engobes are fool-proof, right? Just mix the recipe you found on the internet, or that someone else recommends, and you are good to go. Wrong! Low fire slips need to be compatible with the body in two principle ways: drying and firing. Terra cotta bodies have low shrinkage at cone 06-04 (but high at cone 02). The percentage of frit in the engobe determines its firing shrinkage at each of those temperatures. Too much and the engobe is stretched on, too little and it is under compression. The lower the frit the less the glass-bonding with the body and the more chance of flaking if they do fit well (either during the firing or after the customer stresses your product). The engobe also needs to shrink with the body during drying. How can you measure compatibility? Bi-body strips. First I prepare a plastic sample of the engobe. Then I roll 4 mm thick slabs of it and the body, lay them face-to-face and roll that down to 4 mm again. I cut 2.5x12 cm bars and dry and fire them. The curling indicates misfit. This engobe needs more plastic clay (so it dry-shrinks more) and less frit (to shrink less on firing).

How to test if an engobe fits a clay body

This is part of a project to fit an engobe (slip) onto a terra cotta at cone 02 using the EBCT test.
Left: On drying the red body curls the bi-clay strip toward itself, but on firing it goes the other way!
Right: SHAB test bars of the white slip and red body enable comparing their drying and firing shrinkages.
Center back: A mug with the white engobe and a transparent overglaze. The slip is going translucent under the glaze because it is too vitreous. Its higher fired shrinkage curls the bi-clay bars toward itself. Reducing the frit will reduce the firing shrinkage and make it more opaque (because it will melt less).
Front: A different, more vitreous red body (Zero3 stoneware) fits the slip better (the strips dry and fire straight).

White majolica bases have very, very low melt fluidity

This is Linda Arbuckle's base recipe (66% frit 3124, 23% feldspar, 13 kaolin/bentonite, 9 zircon, 4 tin oxide mixed to 1.62 specific gravity). It is fired at cone 05 creating a super gloss. This is applied very, very thickly (double the thickness of what a stoneware glaze would be). Yet notice how the air-vent holes did not heal during firing, these would have filled in easily had this been on stoneware or porcelain. For this reason, majolica glazes must be applied to ware not having any abrupt concave contours (this also happened on the handle-joins and where foot-meets-wall inside). Bisque must be clean to assure good adherence. Any glaze coverage issues must be repaired carefully before firing. This piece was bisque fired at cone 06, that is the reason for the air vent holes. Had it been bisque fired at cone 04 (higher than the glaze firing) these would not have occurred. However that would have extended the dip-time, this one was held under 10 seconds whereas a cone 04 bisque would have required 20 seconds.

For even coverage white majolica glazes must be applied by dipping

Two white majolica mugs

The mug on the left has three coats of Spectrum Majolica base, painted on by brush. Drying was required after doing the inside coats, so the total glazing time was several hours. The glaze layer is way too thin and it is not even at all! The one on the right was dipped in a 5 gallon bucket-full of G3890 Arbuckle white (that was weighed out according to a recipe and slurried at 1.62 specific gravity). It took seconds to dip-apply, the thickness coverage is good. As is obvious, it makes sense to make your own base white. Then decorate using the overglaze colors (e.g. the Spectrum Majolica series). Another advantage of making your own white is that you can splurge on the amount of opacifier (in this case 9% zircon and 4% tin oxide), to achieve maximum whiteness and opacity. And, you can proportion a mix of two frits (having higher and lower thermal expansion) to fine-tune the fit with the body (a big issue at low fire).

The best way to opacify a low-temperature terra cotta glaze

Opacify a low fire transparent glaze

Tin oxide is a powerful opacifier, but the 5% in this Frit 3124 based Arbuckle Majolica cone 04 recipe on the left is not sufficient. Adding 10% zircon (e.g. Zircopax, Superpax) produces the one on the right. Would just using 15% zircon be better? No. More zircon means a stiffer melt and more issues with crawling (notice the small bare spots on the right edge). This could be managed by the addition of CMC gum or a higher clay content to get better adhesion and dry hardness). But another improvement would be worth trying first: Use 4% tin and 8% zircon. That should opacify enough and present fewer problems with crawling.

Lindsay Montgomery Majolica Plate: Lake of Fire (White Women Elected Trump), 2017

Made from Tucker PHB (tested on our code L4183). Glaze is G3890 Arbuckle majolica recipe. Imagery done using Spectrum Majolica colors (the white tested under our code G3883). Glaze firing temperature is cone 05 (bisque cone 04). "I see medieval symbols as powerful images that we can use to talk about environmental activism today, women's rights today, just all kinds of political ideas about speaking truth to power," she says.

Arbuckle Majolica glaze using Fusion Frit F-19

Majolica glaze tiles

Fusion Frit F-19 is said to be a substitute for Ferro Frit 3124, for this particular glaze that appears to be true. The Arbuckle Majolica glaze was applied on Plainsman L210 and fired at cone 04 (but not as thickly applied as would be customary on Majolica ware). On the left is the one with Ferro Frit 3124, on the right is the one with the F-19. The recipe is based on Ferro Frit 3124 and adds 20% of a feldspar neheline mix (likely to increase thermal expansion because it shivered on the original clay body). It is suspended by 10% kaolin. This may craze on your clay body, the G1916Q thermal expansion adjustable transparent base might be a better solution (it responds similarly to a zircon/tin addition to opacify).

Majolica glaze crawling on this slip-cast terra cotta

Mitigating factors are poor adherence of the glaze to the smooth-surfaced L4170B terra cotta bisque, high zircon content in the glaze (it reduces melt fluidity) and the very thick application (this is a variation on G1916Q as a majolica glaze). Which is the most important of those factors? The adherence to the bisque. An addition of Veegum CER solved the problem (50g of the solution to 0.75 litres of glaze slurry, with added water to thin it out). Unlike with CMC gum, this slurry still goes on thick and evenly. Although the piece on the left is darker red, that is a photo issue, these were both the same body and fired at cone 04.


Glossary Earthenware
What is the difference between earthenware and a regular stoneware body? Earthenwares lack the glass development to fill voids and glue particles.
Glossary Opacifier
Glaze opacity refers to the degree to which it is opaque. Opacifiers are powders added to transparent ceramic glazes to make them opaque.
Glossary Terra Cotta
A type of red firing pottery. Terra cotta clay is available almost everywhere, it is fired at low temperatures. But quality is deceptively difficult to achieve.
Glossary Glaze shivering
Shivering is a ceramic glaze defect that results in tiny flakes of glaze peeling off edges of ceramic ware. It happens because the thermal expansion of the body is too much higher than the glaze.
Articles The Majolica Earthenware Process
How to make strong, durable functional ware from red terra cotta odies based on the traditional of majolica.
Articles G1916M Cone 06-04 transparent glaze
This is a frit based boron glaze that is easily adjustable in thermal expansion, a good base for color and a starting point to go on to more specialized glazes.
Media How to Apply a White Slip to Terra Cotta Ware
I will show you some secrets of making a base engobe (or slip) apply to leather hard terracotta ware in a thick, perfectly even layer.
Linda Arbuckle Majolica glaze recipe
By Tony Hansen
Follow me on

Got a Question?

Buy me a coffee and we can talk, All Rights Reserved
Privacy Policy