GA10-B - Alberta Slip Tenmoku Cone 10R

Modified: 2022-01-30 15:56:22

You can make a tenmoku from Alberta Slip by adding only 2% iron oxide and 5% calcium carbonate

Notes

Tenmoku glazes normally contain 10%+ iron oxide, they are extremely messy to use and often have poor slurry suspension properties and are difficult to apply evenly. This recipe is totally different, it is so much cleaner to use. It applies very evenly and suspends well.

You can adjust the drying hardness, drying shrinkage and suspension properties by adjusting the proportion of calcined to raw Alberta Slip (see the preparation page at http://albertaslip.com for more information). You can change the degree of melting by adjusting the calcium carbonate and the intensity of color by tuning the iron oxide.

Related Information

Which tenmoku base is better: Alberta Slip or a clear glaze?

This picture has its own page with more detail, click here to see it.

Right: Alberta slip is almost a Tenmoku glaze by itself at cone 10 reduction. To go all the way only 1-2% more iron is needed (plus a little extra flux for melt fluidity, perhaps 5% calcium carbonate). Compare that to crow-baring a clear glaze into a tenmoku (left): This is G1947U plus 11% red iron oxide. That produces a slurry that is miserable to work with (it stains everything it comes into contact with) and turns into a jelly on standing.

Ravenscrag Tenmoku vs. Alberta Slip Tenmoku on porcelain

This picture has its own page with more detail, click here to see it.

Body is Plainsman P580. Far left: G2894 Ravenscrag Tenmoku with 10% whiting and 10% iron oxide added. Center: Pure Alberta Slip plus 5% whiting and 1% iron oxide. Right: Pure Alberta Slip plus 5% whiting and and 2% iron. The Alberta Slip versions are less messy to use because so much less iron is needed (iron also causes the slurry to gel). The Ravenscrag and higher iron Alberta Slip versions are running, they are too fluid. The rust colored crystals are not developing the way they did with these glazes on an iron stoneware (in the same firing).

Ravenscrag Tenmoku vs. Alberta Slip Tenmoku

This picture has its own page with more detail, click here to see it.

All of these are on a cone 10 reduction fired iron stoneware (Plainsman H443). Far left: G2894 Ravenscrag Tenmoku with 10% whiting and 10% iron oxide added. Center: Pure Alberta Slip plus 5% whiting and 1% iron oxide. Right: Pure Alberta Slip plus 5% whiting and and 2% iron. The Alberta Slip versions are less messy to use because so much less iron is needed (iron also causes the slurry to gel). The Ravenscrag version is running, it is too fluid. Likely 5% calcium carbonate would be enough (and maybe less iron).

Tenmokus made from Alberta Slip and Ravenscrag Slip

This picture has its own page with more detail, click here to see it.

GR10-K1 Cone 10R Ravenscrag Tenmoku (right) compared to Tenmoku made from Alberta Slip (left, it is 91% Alberta Slip with 5% added calcium carbonate and 2% iron oxide). Left is Plainsman P700 porcelain, right is H570. Tenmokus are popular for the way they break to a crystalline light brown on the edges of contours.

Alberta slip vs Alberta Slip tenmoku

This picture has its own page with more detail, click here to see it.

Alberta Slip 100% (left) and Alberta Slip Tenmoku (right). The tenmoku is a little more opaque and forms the characteristic brown crystals on edges of contours (e.g. rim).

Roasting Alberta and Ravenscrag Slips at 1000F: Essential for good glazes

This picture has its own page with more detail, click here to see it.

Roasted Alberta Slip (right) and raw powder (left). These are thin-walled 5 inch cast bowls, each holds about 1 kg. I hold the kiln at 1000F for 30 minutes. Why do this? Because Alberta Slip is a clay, it shrinks on drying (if used raw the GA6-B and similar recipes will crack as they dry and then crawl during firing). Roasting eliminates that. Calcining to 1850F sinters some particles together (creating a gritty material) while roasting to 1000F produces a smooth, fluffy powder. Technically, Alberta Slip losses 3% of its weight on roasting so I should use 3% less than a recipe calls for. But I often just swap them gram-for-gram.

Links

XML to Paste Into Insight-live

<?xml version="1.0"?>
<recipes version="1.0" encoding="UTF-8">
<recipe name="Alberta Slip Tenmoku Cone 10R" keywords="You can make a tenmoku from Alberta Slip by adding only 2% iron oxide and 5% calcium carbonate" id="32" date="2022-01-30" codenum="GA10-B" altcodenum="G2880B">
<recipelines>
<recipeline material="Alberta Slip 1000F Roasted" amount="50.000"/>
<recipeline material="Alberta Slip" amount="50.000"/>
<recipeline material="Calcium Carbonate" amount="5.000" added="1"/>
<recipeline material="Red Iron Oxide" amount="2.000" added="1"/>
<url url="https://digitalfire.com/recipe/32" descrip="https://digitalfire.com/recipe/32"/>
</recipelines>
<urls/>
</recipe>
</recipes>

By Tony Hansen Follow me on

Got a Question?

Buy me a coffee and we can talk