Ag2O | AlF3 | As2O3 | As4O6 | Au2O3 | BaF2 | BeO | CaF2 | CdO | CeO2 | CrO3 | Cs2O | Cu2O | CuCO3 | Dy2O3 | Er2O3 | Eu2O3 | F | Fr2O | Free SiO2 | Ga2O3 | GdO3 | GeO2 | HfO2 | HgO | Ho2O3 | In2O3 | IrO2 | KF | KNaO | La2O3 | Lu2O3 | Mn2O3 | MnO2 | MoO3 | N2O5 | NaF | Nb2O5 | Nd2O3 | NiO | OsO2 | P2O5 | Pa2O5 | PbF2 | PdO | PmO3 | PO4 | Pr2O3 | PrO2 | PtO2 | RaO | Rb2O | Re2O7 | RhO3 | RuO2 | Sb2O3 | Sb2O5 | Sc2O3 | Se | SeO2 | Sm2O3 | Ta2O5 | Tb2O3 | Tc2O7 | ThO2 | Tl2O | Tm2O3 | U3O8 | UO2 | WO3 | Y2O3 | Yb2O3 | ZrO
•The secret to cool bodies and glazes is a lot of testing.
•The secret to know what to test is material and chemistry knowledge.
•The secret to learning from testing is documentation.
•The place to test, do the chemistry and document is an account at https://insight-live.com
•The place to get the knowledge is https://digitalfire.com
Sign-up at https://insight-live.com today.
|COLE - Co-efficient of Linear Expansion||0.129|
|GSPT - Frit Softening Point||1923C|
-Together with CaO, SrO, and MgO it is considered one of the alkaline earth GROUP of oxides. It has a cubic crystal structure.
-Baria is the heaviest of the divalent fluxing oxides.
-Barium gives unique color responses with certain oxides (e.g. with copper it will give a marked blue compared to glazes fluxed with MgO, SrO).
-BaO often contributes a high index of refraction and this can enhance in-glaze colors.
-As a flux it can be very active in small amounts (not active at low temperatures). For example, it can improve gloss, elasticity, mechanical strength and corrosion resistance, and acid resistance.
-Barium imparts properties to glazes that fall between calcia/magnesia and lead (it tends to produce a denser, more brilliant but less durable product than calcia). Barium does not reduce in the melt and therefore does not discolor. It acts as a flux (if decomposed) and can assist in the formation of a matte structure. Barium forms silicates slowly, but when completely combined it is very active as a fluxing agent.
-Baria is more effective as a melter when associated with other fluxing oxides with which it can combine (e.g. if fused in certain frit formulations it can react readily in even low temperature glazes). It is known, for example, to form a strong eutectic with B2O3 to produce glossy and runny glazes that can solidify below 500C).
-In larger amounts it becomes refractory and can produce dangerous leachable glazes, since it does not fully combine to form insoluble silicates. It is common to see art glazes with more than 20% barium carbonate, and at times, even 40-50% recipes are traded in the pottery community. These are almost certainly leachable.
-Use with caution in functional ware! There is considerable controversy concerning the safety of barium in glazes (i.e. if you see larger amounts of barium in glazes labeled 'Dry Matte' or 'Stony Matt', be very cautious). Like lead, it can be leached FROM the surface (of improperly fired or formulated glazes) by acidic foods or liquids. Government agencies have the power to levy fines if glaze is found to be soluble.
-If possible, determine the reason for BaO in the recipe. The mechanism may well be better accomplished by another oxide. For example, SrO and CaO can both be employed to produce crystal mattes in saturation (although a calcium matte will likely be coarser). K2O may produce a better blue with copper or a brighter color.
-SrO has been promoted as a glaze substitute for BaO and in some cases this is true. It has a lower disassociation temperature and reacts earlier and is potentially able to produce a more perfect surface (unmarred by the bubbles and pits associated with higher temperature decomposition). Still it is best to substitute BaO on a 'mechanism' basis, that is, understand why it is there and choosing the best alternate oxide based on that. In some cases, even CaO or MgO can be substituted.
-Used in optical glass (up to 30%),
-Used in small amounts in bottle and flat glass (.5%),
-It is in common use in glass formulations in the television tube industry.
-It can produce better translucency in porcelain bodies.
-It is used to provide maximum flux density in hard-core permanent magnets.
-In enamels its acts as a strong flux and is less expensive than lead or zinc. It does not reduce in the presence of iron high in carbon however it is sensitive to the presence of sulfur (i.e. an impurity in antimony).
-Used in pressed glass tableware it renders brilliance and finish, but detrimentally affects certain other mechanical properties.
Glaze Color - Turquoise
Barium glazes are well known for thier ability to produce matte turquoise colors with copper. While strontium is often used to duplicate the matte texture of barium it does not have the same color response.
Glaze Matteness - Micro Crystalline
Baria is well known for its tendency to cause the growth of a fine mesh of micro crystals to produce a silky matte texture.
Left: G2934 magnesia cone 6 matte (sold by Plainsman Clays). Right (G2934D): The same glaze, but with 0.4 molar of BaO (from Ferro Frit CC-257) substituted for the 0.4 MgO it had. The MgO is the mechanism of the matte effect. Barium also creates mattes, but only if the chemistry of the host glaze and the temperature are right. In addition, barium mattes are normally made using the raw carbonate form, not a frit. In fritted form, barium can be a powerful flux when well dissolved in the melt and boron is present. This glaze is actually remarkably transparent. However, if this was fired lower it could very well matte.
All common traditional ceramic base glazes are made from only a dozen elements (plus oxygen). Materials decompose when glazes melt, sourcing these elements in oxide form. The kiln builds the glaze from these, it does not care what material sources what oxide (assuming, of course, that all materials do melt or dissolve completely into the melt to release those oxides). Each of these oxides contributes specific properties to the glass. So, you can look at a formula and make a good prediction of the properties of the fired glaze. And know what specific oxide to increase or decrease to move a property in a given direction (e.g. melting behavior, hardness, durability, thermal expansion, color, gloss, crystallization). And know about how they interact (affecting each other). This is powerful. And it is simpler than looking at glazes as recipes of hundreds of different materials (each sources multiple oxides so adjusting it affects multiple properties).
Out Bound Links
Barium Carb, Witherite
Calk, Calk-Stone, Barite, Barytes, BaSO4, Barium Sulphate
The term 'limit formula' historically has typically referred to efforts to establish absolute ranges for mixtures of oxides that melt well at an intended temperature and are not in sufficient excess to cause defects. These formulas typically show ranges for each oxide commonly used in a specific gla...
In Bound Links
Hazards of barium carbonate, considerations regarding its use in clay bodies for precipitation of soluble salts
Glaze chemistry models fired glazes as constructed of oxides decomposed from the materials in the recipe. Fired properties of glazes (like melting temperature, thermal expansion, surface character, even color) are a product of the oxide makeup (the chemistry). Oxides are grouped in various ways to s...
On the theoretical glaze chemistry level, a flux is an oxide that lowers the melting or softening temperature of a mix of materials. Fluxes are interactors (they often melt poorly on their own but react strongly with high melting materials where Al2O3/SiO2 predominate). There are less than ten commo...