Pemco Frit Pb-1114

Calcium borosilite medium lead frit for cone 08-04 glazes

Alternate Names: Frit Pb1114

OxideAnalysisFormula
CaO9.80%0.483
K2O1.40%0.041
Na2O1.90%0.085
PbO31.60%0.391
Al2O33.50%0.095
B2O311.10%0.441
SiO240.70%1.872
Oxide Weight276.42
Formula Weight276.42
If this formula is not unified correctly please contact us.
COLE - Co-efficient of Linear Expansion 7.00
GSPT - Frit Softening Point 1400F
MLRG - Frit Melting Range (C) 1350-1500F
IFP - I.F.P. (celsius) 600C

Good for low temperature, clear and colored glazes. Can be blended with Pb-349, Pb-1241 or Pb-1421 for intermediate temperatures.


Out Bound Links

In Bound Links


By Tony Hansen

XML for Import into INSIGHT

<?xml version="1.0" encoding="UTF-8"?> <material name="Pemco Frit Pb-1114" descrip="Calcium borosilite medium lead frit for cone 08-04 glazes" searchkey="Frit Pb1114" loi="0.00" casnumber="65997-18-4"> <oxides> <oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="9.800" tolerance=""/> <oxide symbol="K2O" name="Potassium Oxide" status="" percent="1.400" tolerance=""/> <oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="1.900" tolerance=""/> <oxide symbol="PbO" name="Lead Oxide" status="" percent="31.600" tolerance=""/> <oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="3.500" tolerance=""/> <oxide symbol="B2O3" name="Boric Oxide" status="" percent="11.100" tolerance=""/> <oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="40.700" tolerance=""/> </oxides> </material>


Feedback, Suggestions

Your email address

Subject

Your Name

Message


Copyright 2003, 2008, 2015 https://digitalfire.com, All Rights Reserved