IMCO Burgundy

Earthenware and middle fire red burning clay

Oxide Weight561.08
Formula Weight605.26
If this formula is not unified correctly please contact us.

Burgundy is an iron bearing, silty clay recommended for low and mid range firing applications.
Recommended as a substitute for Banta Red.

Sieve analysis: 0.1% on 80 mesh, 8.8% on 200 mesh
Dry color: Yellow-brown
Drying shrinkage: 8%
Fired shrinkage: Cone 05 - 8.5%, cone 1 - 12%, cone 5 - 15.3%
Porosity: Cone 05 - 15.4%, cone 1 - 8.2%, cone 5 - 9%

Out Bound Links

By Tony Hansen

XML for Import into INSIGHT

<?xml version="1.0" encoding="UTF-8"?> <material name="IMCO Burgundy" descrip="Earthenware and middle fire red burning clay" searchkey="" loi="0.00" casnumber=""> <oxides> <oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="2.090" tolerance=""/> <oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="3.110" tolerance=""/> <oxide symbol="K2O" name="Potassium Oxide" status="" percent="2.100" tolerance=""/> <oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="1.400" tolerance=""/> <oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.680" tolerance=""/> <oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="15.900" tolerance=""/> <oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="58.200" tolerance=""/> <oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="5.900" tolerance=""/> </oxides> <volatiles> <volatile symbol="LOI" name="Loss on Ignition" percent="7.300" tolerance=""/> </volatiles> </material>

Feedback, Suggestions

Your email address


Your Name


Copyright 2003, 2008, 2015 https://digitalfire.com, All Rights Reserved