Ferro Frit 3565

Low lead calcium borosilicate cone 01-5 glaze frit

OxideAnalysisFormula
CaO9.90%0.577
K2O3.00%0.104
Na2O1.60%0.084
PbO16.00%0.234
Al2O35.60%0.180
B2O37.80%0.366
SiO254.00%2.938
ZrO22.10%0.056
Oxide Weight327.00
Formula Weight327.00
If this formula is not unified correctly please contact us.
COLE - Co-efficient of Linear Expansion 7.2
MLRG - Frit Melting Range (C) 1600F

Use for cone 01-5 dinnerware glazes and general pottery glazes. Considered a safe lead frit. Contains a small amount of zircon that substitutes might not have.


Out Bound Links

In Bound Links


By Tony Hansen

XML for Import into INSIGHT

<?xml version="1.0" encoding="UTF-8"?> <material name="Ferro Frit 3565" descrip="Low lead calcium borosilicate cone 01-5 glaze frit" searchkey="" loi="0.00" casnumber="65997-18-4"> <oxides> <oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="9.900" tolerance=""/> <oxide symbol="K2O" name="Potassium Oxide" status="" percent="3.000" tolerance=""/> <oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="1.600" tolerance=""/> <oxide symbol="PbO" name="Lead Oxide" status="" percent="16.000" tolerance=""/> <oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="5.600" tolerance=""/> <oxide symbol="B2O3" name="Boric Oxide" status="" percent="7.800" tolerance=""/> <oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="54.000" tolerance=""/> <oxide symbol="ZrO2" name="Zirconium Dioxide" status="" percent="2.100" tolerance=""/> </oxides> </material>


Feedback, Suggestions

Your email address

Subject

Your Name

Message


Copyright 2003, 2008, 2015 https://digitalfire.com, All Rights Reserved