Cedar Heights Fireclay

Fire Clay

OxideAnalysisFormula
CaO0.57%0.047
MgO0.11%0.013
Na2O0.50%0.037
TiO20.31%0.018
Al2O322.06%1.000
SiO266.62%5.125
Fe2O31.70%0.049
LOI8.13
Oxide Weight424.78
Formula Weight462.38
If this formula is not unified correctly please contact us.
PCE - Pyrometric Cone Equivalent 30

A raw clay similar to the more well known Goldart. It is used in the formulation of middle and high temperature stoneware clay bodies. It's non-uniform texture and firing properties make for interesting fired surfaces.


Out Bound Links

In Bound Links


By Tony Hansen

XML for Import into INSIGHT

<?xml version="1.0" encoding="UTF-8"?> <material name="Cedar Heights Fireclay" descrip="Fire Clay" searchkey="" loi="8.13" casnumber="70694-09-6"> <oxides> <oxide symbol="CaO" name="Calcium Oxide, Calcia" status="" percent="0.570" tolerance=""/> <oxide symbol="MgO" name="Magnesium Oxide, Magnesia" status="" percent="0.110" tolerance=""/> <oxide symbol="Na2O" name="Sodium Oxide, Soda" status="" percent="0.500" tolerance=""/> <oxide symbol="TiO2" name="Titanium Dioxide, Titania" status="" percent="0.310" tolerance=""/> <oxide symbol="Al2O3" name="Aluminum Oxide, Alumina" status="" percent="22.060" tolerance=""/> <oxide symbol="SiO2" name="Silicon Dioxide, Silica" status="" percent="66.620" tolerance=""/> <oxide symbol="Fe2O3" name="Iron Oxide, Ferric Oxide" status="" percent="1.700" tolerance=""/> </oxides> <volatiles> <volatile symbol="LOI" name="Loss on Ignition" percent="8.130" tolerance=""/> </volatiles> </material>


Feedback, Suggestions

Your email address

Subject

Your Name

Message


Copyright 2003, 2008, 2015 https://digitalfire.com, All Rights Reserved